| Technical Description | A high-clarity raw material that can be chemically smoothed using alcohol aerosols to achieve a glass-like finish for luxury consumer liquid containers. |
| Base Polymer | Polyvinyl Butyral |
| Density (g/cm3) | 1.1 |
| Tensile Strength (MPa) | 40 |
| Flexural Modulus (MPa) | 2050 |
| Elongation at Break (%) | 18 |
| Izod Impact Strength (J/m) | 65 |
| Glass Transition Temp (°C) | 72 |
| Melting Point (°C) | 165 |
| Printing Temp (°C) | 190 - 220 |
| Build Plate Temp (°C) | 60 - 75 |
| Thermal Conductivity (W/m⋅K) | 0.16 |
| Water Absorption (%) | 1.2 |
| Linear Mold Shrinkage (%) | 0.45 |
| Hardness (Shore D) | 72 |
| Odor Level | Low |
| Chemical Resistance | Alcohol Soluble |
| UV Stability | High |
| Transparency Level | 0.91 |
| Surface Tension (mN/m) | 34 |
| Recommended Speed (mm/s) | 40 - 70 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Fan Cooling (%) | 50 |
| Shelf Life (Months) | 12 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Decorative Spirit Bottles |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.