Cat No:SSM-0031
Description
Inorganic alumina-filled support designed to maintain shape during high-vacuum sintering of stainless steel and tool steel parts.
| Base Material | Alumina-Polymer Composite |
| Solubility Method | Thermal/Mechanical |
| Solvent Type | None |
| Heat Deflection Temp (0.45MPa) | 350+ |
| Glass Transition Temp (Tg) | 380 |
| Melting Point (°C) | - |
| Density (g/cm³) | 2.85 |
| Water Absorption (%) | 0.01 |
| Tensile Strength (MPa) | 42 |
| Tensile Modulus (MPa) | 8500 |
| Elongation at Break (%) | 1 |
| Flexural Strength (MPa) | 85 |
| Flexural Modulus (MPa) | 7800 |
| Printing Temp (°C) | 320-350 |
| Bed Temp (°C) | 120-150 |
| Chamber Temp (°C) | 100-140 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.15 |
| Shrinkage Rate (%) | 0.02 |
| Continuous Use Temp (°C) | 300 |
| Impact Strength (kJ/m²) | 4.5 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.