Cat No:CRSM-0097
Description
High-toughness aramid-PPA composite, combining the heat stability of PPA with the non-brittle failure characteristics of aramid fiber.
| Base Material | Polyphthalamide |
| Reinforcement Type | Para-aramid Fiber |
| Reinforcement Volume (%) | 0.15 |
| Density (g/cm³) | 1.28 |
| Tensile Strength (MPa) | 98 |
| Tensile Modulus (MPa) | 6800 |
| Elongation at Break (%) | 5.5 |
| Flexural Strength (MPa) | 155 |
| Flexural Modulus (MPa) | 6200 |
| Heat Deflection Temp (0.45MPa) | 255 |
| Glass Transition Temp (Tg) | 125 |
| Melting Point (°C) | 310 |
| Thermal Conductivity (W/mK) | 0.25 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^16 |
| Water Absorption (%) | 0.3 |
| Printing Temp (°C) | 310-340 |
| Bed Temp (°C) | 100-130 |
| Chamber Temp (°C) | 80-110 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.15 |
| Shrinkage Rate (%) | 0.25 |
| Continuous Use Temp (°C) | 175 |
| Impact Strength (kJ/m²) | 22 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|