| Technical Description | Sustainable bio-composite raw material infused with natural fibers to provide a wood-like texture and scent for luxury home décor and lifestyle products. |
| Base Polymer | PLA + Wood Fiber |
| Density (g/cm3) | 1.18 |
| Tensile Strength (MPa) | 32 |
| Flexural Modulus (MPa) | 2900 |
| Elongation at Break (%) | 4 |
| Izod Impact Strength (J/m) | 25 |
| Glass Transition Temp (°C) | 55 |
| Melting Point (°C) | 150 |
| Printing Temp (°C) | 190 - 220 |
| Build Plate Temp (°C) | 50 - 60 |
| Thermal Conductivity (W/m⋅K) | 0.14 |
| Water Absorption (%) | 1.25 |
| Linear Mold Shrinkage (%) | 0.25 |
| Hardness (Shore D) | 75 |
| Odor Level | Wood Scent |
| Chemical Resistance | Low |
| UV Stability | Low |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 36 |
| Recommended Speed (mm/s) | 40 - 70 |
| Layer Resolution (mm) | 0.20 - 0.35 |
| Fan Cooling (%) | 100 |
| Shelf Life (Months) | 12 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Aesthetic Household Goods |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.