Cat No:SSM-0041
Description
Biocompatible sacrificial material designed for tissue engineering scaffolds, allowing for slow dissolution in physiological fluids.
| Base Material | PCL-Based Polymer |
| Solubility Method | Hydrolysis |
| Solvent Type | Phosphate Buffered Saline |
| Heat Deflection Temp (0.45MPa) | 45 |
| Glass Transition Temp (Tg) | -60 |
| Melting Point (°C) | 60 |
| Density (g/cm³) | 1.14 |
| Water Absorption (%) | 1 |
| Tensile Strength (MPa) | 18 |
| Tensile Modulus (MPa) | 450 |
| Elongation at Break (%) | 600 |
| Flexural Strength (MPa) | 25 |
| Flexural Modulus (MPa) | 400 |
| Printing Temp (°C) | 80-120 |
| Bed Temp (°C) | 30-45 |
| Chamber Temp (°C) | - |
| Fan Speed (%) | 100 |
| Nozzle Type | Brass |
| Layer Height (mm) | 0.1 |
| Shrinkage Rate (%) | 1.5 |
| Continuous Use Temp (°C) | 35 |
| Impact Strength (kJ/m²) | 55 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.