Cat No:CRSM-0011
Description
High-performance amorphous thermoplastic reinforced with carbon fiber for superior dimensional stability and inherent flame retardancy.
| Base Material | Polyethersulfone |
| Reinforcement Type | Chopped Carbon Fiber |
| Reinforcement Volume (%) | 0.15 |
| Density (g/cm³) | 1.42 |
| Tensile Strength (MPa) | 98 |
| Tensile Modulus (MPa) | 7200 |
| Elongation at Break (%) | 2.2 |
| Flexural Strength (MPa) | 145 |
| Flexural Modulus (MPa) | 6800 |
| Heat Deflection Temp (0.45MPa) | 215 |
| Glass Transition Temp (Tg) | 225 |
| Melting Point (°C) | - |
| Thermal Conductivity (W/mK) | 0.32 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^6 - 10^8 |
| Water Absorption (%) | 0.35 |
| Printing Temp (°C) | 360-390 |
| Bed Temp (°C) | 140-160 |
| Chamber Temp (°C) | 100-140 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.15 |
| Shrinkage Rate (%) | 0.35 |
| Continuous Use Temp (°C) | 185 |
| Impact Strength (kJ/m²) | 8 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.