Cat No:CRSM-0073
Description
Medical-grade compatible PEEK composite with high carbon fiber loading for bone-equivalent stiffness in orthopedic and prosthetic research.
| Base Material | PEEK |
| Reinforcement Type | Chopped Carbon Fiber |
| Reinforcement Volume (%) | 0.3 |
| Density (g/cm³) | 1.42 |
| Tensile Strength (MPa) | 195 |
| Tensile Modulus (MPa) | 18000 |
| Elongation at Break (%) | 1.5 |
| Flexural Strength (MPa) | 285 |
| Flexural Modulus (MPa) | 16500 |
| Heat Deflection Temp (0.45MPa) | 320 |
| Glass Transition Temp (Tg) | 143 |
| Melting Point (°C) | 343 |
| Thermal Conductivity (W/mK) | 0.52 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^5 - 10^7 |
| Water Absorption (%) | 0.08 |
| Printing Temp (°C) | 410-450 |
| Bed Temp (°C) | 130-160 |
| Chamber Temp (°C) | 110-150 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.1 |
| Shrinkage Rate (%) | 0.1 |
| Continuous Use Temp (°C) | 260 |
| Impact Strength (kJ/m²) | 18 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|