Cat No:CRSM-0079
Description
Dynamic vulcanizate composite with carbon fiber, providing high elasticity and chemical resistance for automotive seals and vibration isolators.
| Base Material | TPV |
| Reinforcement Type | Chopped Carbon Fiber |
| Reinforcement Volume (%) | 0.1 |
| Density (g/cm³) | 1.12 |
| Tensile Strength (MPa) | 32 |
| Tensile Modulus (MPa) | 1100 |
| Elongation at Break (%) | 120 |
| Flexural Strength (MPa) | 45 |
| Flexural Modulus (MPa) | 980 |
| Heat Deflection Temp (0.45MPa) | 105 |
| Glass Transition Temp (Tg) | -45 |
| Melting Point (°C) | - |
| Thermal Conductivity (W/mK) | 0.42 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^6 - 10^8 |
| Water Absorption (%) | 0.08 |
| Printing Temp (°C) | 235-260 |
| Bed Temp (°C) | 50-80 |
| Chamber Temp (°C) | - |
| Fan Speed (%) | 40 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 1.1 |
| Continuous Use Temp (°C) | 115 |
| Impact Strength (kJ/m²) | 55 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|