| Technical Description | A lightweight, carbon-fiber reinforced polyolefin raw material providing high stiffness and chemical inertness for structural consumer outdoor equipment. |
| Base Polymer | PP + 20% CF |
| Density (g/cm3) | 1.08 |
| Tensile Strength (MPa) | 48 |
| Flexural Modulus (MPa) | 4200 |
| Elongation at Break (%) | 6 |
| Izod Impact Strength (J/m) | 95 |
| Glass Transition Temp (°C) | 5 |
| Melting Point (°C) | 165 |
| Printing Temp (°C) | 240 - 265 |
| Build Plate Temp (°C) | 90 - 110 |
| Thermal Conductivity (W/m⋅K) | 0.38 |
| Water Absorption (%) | 0.02 |
| Linear Mold Shrinkage (%) | 0.25 |
| Hardness (Shore D) | 76 |
| Odor Level | Mild |
| Chemical Resistance | High (Alkalis) |
| UV Stability | Moderate |
| Transparency Level | Opaque (Black) |
| Surface Tension (mN/m) | 33 |
| Recommended Speed (mm/s) | 30 - 55 |
| Layer Resolution (mm) | 0.15 - 0.30 |
| Shelf Life (Months) | 24 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Structural Sporting Gear |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.