| Technical Description | A heavyweight composite raw material that mimics the feel and finish of fired ceramic, perfect for luxury consumer homeware and architectural prototypes. |
| Base Polymer | PLA + 20% Ceramic |
| Density (g/cm3) | 1.45 |
| Tensile Strength (MPa) | 40 |
| Flexural Modulus (MPa) | 4500 |
| Elongation at Break (%) | 2 |
| Izod Impact Strength (J/m) | 20 |
| Glass Transition Temp (°C) | 58 |
| Melting Point (°C) | 160 |
| Printing Temp (°C) | 205 - 230 |
| Build Plate Temp (°C) | 50 - 60 |
| Thermal Conductivity (W/m⋅K) | 0.3 |
| Water Absorption (%) | 0.5 |
| Linear Mold Shrinkage (%) | 0.15 |
| Hardness (Shore D) | 84 |
| Odor Level | Extremely Low |
| Chemical Resistance | Low |
| UV Stability | Moderate |
| Transparency Level | Opaque (White) |
| Surface Tension (mN/m) | 40 |
| Recommended Speed (mm/s) | 30 - 55 |
| Layer Resolution (mm) | 0.15 - 0.30 |
| Fan Cooling (%) | 100 |
| Shelf Life (Months) | 12 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Premium Tableware Models |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.