Cat No:SSM-0072
Description
Sacrificial core for metal investment casting, offering high thermal stability and easy removal via caustic leaching.
| Base Material | Silica-Binder Composite |
| Solubility Method | Chemical Leaching |
| Solvent Type | Caustic Solution |
| Heat Deflection Temp (0.45MPa) | 450 |
| Glass Transition Temp (Tg) | - |
| Melting Point (°C) | - |
| Density (g/cm³) | 2.15 |
| Water Absorption (%) | 0.02 |
| Tensile Strength (MPa) | 15 |
| Tensile Modulus (MPa) | 6200 |
| Elongation at Break (%) | 0.5 |
| Flexural Strength (MPa) | 45 |
| Flexural Modulus (MPa) | 5800 |
| Printing Temp (°C) | 300-340 |
| Bed Temp (°C) | 120-150 |
| Chamber Temp (°C) | 100-140 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.02 |
| Continuous Use Temp (°C) | 400 |
| Impact Strength (kJ/m²) | 2 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.