Cat No:SSM-0032
Description
Specifically engineered brittle sacrificial material for pressure vessel winding; designed to shatter and be removed easily after curing.
| Base Material | Modified Brittle Copolymer |
| Solubility Method | Mechanical/Crushing |
| Solvent Type | None |
| Heat Deflection Temp (0.45MPa) | 105 |
| Glass Transition Temp (Tg) | 115 |
| Melting Point (°C) | 220 |
| Density (g/cm³) | 1.12 |
| Water Absorption (%) | 0.1 |
| Tensile Strength (MPa) | 25 |
| Tensile Modulus (MPa) | 4500 |
| Elongation at Break (%) | 1.5 |
| Flexural Strength (MPa) | 35 |
| Flexural Modulus (MPa) | 4200 |
| Printing Temp (°C) | 240-270 |
| Bed Temp (°C) | 90-110 |
| Chamber Temp (°C) | 60-80 |
| Fan Speed (%) | 10 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.3 |
| Continuous Use Temp (°C) | 90 |
| Impact Strength (kJ/m²) | 2.5 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.