Description
Support material that becomes extremely brittle under cryogenic cooling, allowing for instant "snap-off" removal without tools.
| Base Material | Modified Polyolefin |
| Solubility Method | Mechanical |
| Solvent Type | None (Brittle at Low Temp) |
| Heat Deflection Temp (0.45MPa) | 95 |
| Glass Transition Temp (Tg) | 105 |
| Melting Point (°C) | 190 |
| Density (g/cm³) | 0.92 |
| Water Absorption (%) | 0.01 |
| Tensile Strength (MPa) | 22 |
| Tensile Modulus (MPa) | 1200 |
| Elongation at Break (%) | 15 |
| Flexural Strength (MPa) | 38 |
| Flexural Modulus (MPa) | 1050 |
| Printing Temp (°C) | 210-240 |
| Bed Temp (°C) | 80-100 |
| Chamber Temp (°C) | 60 |
| Fan Speed (%) | 20 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 1.2 |
| Continuous Use Temp (°C) | 90 |
| Impact Strength (kJ/m²) | 20 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^16 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.