| Technical Description | A specialized PLA-based raw material that increases its heat deflection temperature significantly after a post-print annealing process. |
| Base Polymer | Annealable PLA Blend |
| Density (g/cm3) | 1.24 |
| Tensile Strength (MPa) | 65 |
| Flexural Modulus (MPa) | 3800 |
| Elongation at Break (%) | 4 |
| Izod Impact Strength (J/m) | 35 |
| Glass Transition Temp (°C) | 60 |
| Melting Point (°C) | 175 |
| Printing Temp (°C) | 210 - 230 |
| Build Plate Temp (°C) | 50 - 60 |
| Thermal Conductivity (W/m⋅K) | 0.15 |
| Water Absorption (%) | 0.45 |
| Linear Mold Shrinkage (%) | 0.25 |
| Hardness (Shore D) | 84 |
| Odor Level | Neutral |
| Chemical Resistance | Moderate |
| UV Stability | Moderate |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 38 |
| Recommended Speed (mm/s) | 40 - 90 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Fan Cooling (%) | 100 |
| Shelf Life (Months) | 24 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Hot Beverage Lids |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.