| Technical Description | A 100% bio-sourced Nylon 11 raw material reinforced with carbon fiber, providing extreme stiffness and heat resistance for industrial coffee machine gears. |
| Base Polymer | Polyamide 11 + 30% CF |
| Density (g/cm3) | 1.25 |
| Tensile Strength (MPa) | 115 |
| Flexural Modulus (MPa) | 9200 |
| Elongation at Break (%) | 3.5 |
| Izod Impact Strength (J/m) | 90 |
| Glass Transition Temp (°C) | 48 |
| Melting Point (°C) | 205 |
| Printing Temp (°C) | 265 - 295 |
| Build Plate Temp (°C) | 90 - 110 |
| Thermal Conductivity (W/m⋅K) | 0.42 |
| Water Absorption (%) | 0.15 |
| Linear Mold Shrinkage (%) | 0.1 |
| Hardness (Shore D) | 84 |
| Odor Level | None |
| Chemical Resistance | Exceptional (Oils) |
| UV Stability | High |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 48 |
| Recommended Speed (mm/s) | 20 - 45 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Shelf Life (Months) | 24 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | High-Load Coffee Gears |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.