| Technical Description | A high-resolution liquid raw material designed for vat photopolymerization, providing optical clarity and biocompatibility for personal dental tools. |
| Base Polymer | Clear SLA Photopolymer |
| Density (g/cm3) | 1.15 |
| Tensile Strength (MPa) | 55 |
| Flexural Modulus (MPa) | 2400 |
| Elongation at Break (%) | 12 |
| Izod Impact Strength (J/m) | 30 |
| Glass Transition Temp (°C) | 85 |
| Melting Point (°C) | N/A |
| Printing Temp (°C) | Ambient |
| Build Plate Temp (°C) | N/A |
| Thermal Conductivity (W/m⋅K) | 0.18 |
| Water Absorption (%) | 0.35 |
| Linear Mold Shrinkage (%) | 0.5 |
| Hardness (Shore D) | 84D |
| Odor Level | Low |
| Chemical Resistance | Good |
| UV Stability | High |
| Transparency Level | 0.92 |
| Surface Tension (mN/m) | 37 |
| Recommended Speed (mm/s) | 10-25s/layer |
| Layer Resolution (mm) | 0.025 - 0.10 |
| Fan Cooling (%) | N/A |
| Shelf Life (Months) | 12 |
| Raw Material Diameter (mm) | Liquid |
| Primary Application | Dental Consumer Goods |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.