Cat No:SSM-0088
Description
Sacrificial system that generates controlled gas upon heat-treatment, causing it to collapse/spall from internal voids.
| Base Material | Foaming Polymer |
| Solubility Method | Thermal |
| Solvent Type | Pyrolysis |
| Heat Deflection Temp (0.45MPa) | 120 |
| Glass Transition Temp (Tg) | 135 |
| Melting Point (°C) | 190 |
| Density (g/cm³) | 0.85 |
| Water Absorption (%) | 0.02 |
| Tensile Strength (MPa) | 15 |
| Tensile Modulus (MPa) | 1100 |
| Elongation at Break (%) | 12 |
| Flexural Strength (MPa) | 25 |
| Flexural Modulus (MPa) | 900 |
| Printing Temp (°C) | 210-240 |
| Bed Temp (°C) | 60-90 |
| Chamber Temp (°C) | 40-70 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.3 |
| Shrinkage Rate (%) | 0.1 |
| Continuous Use Temp (°C) | 100 |
| Impact Strength (kJ/m²) | 2 |
| Flame Retardancy (UL94) | V-1 |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.