Cat No:SSM-0058
Description
Inorganic sacrificial material for supporting glass-ceramic 3D printing; stable through the entire debinding and crystallization cycle.
| Base Material | Glass-Polymer Matrix |
| Solubility Method | Thermal/Chemical |
| Solvent Type | Dilute Acid |
| Heat Deflection Temp (0.45MPa) | 220 |
| Glass Transition Temp (Tg) | 240 |
| Melting Point (°C) | - |
| Density (g/cm³) | 2.1 |
| Water Absorption (%) | 0.02 |
| Tensile Strength (MPa) | 65 |
| Tensile Modulus (MPa) | 9500 |
| Elongation at Break (%) | 0.8 |
| Flexural Strength (MPa) | 130 |
| Flexural Modulus (MPa) | 8800 |
| Printing Temp (°C) | 300-340 |
| Bed Temp (°C) | 120-150 |
| Chamber Temp (°C) | 100-140 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.15 |
| Shrinkage Rate (%) | 0.08 |
| Continuous Use Temp (°C) | 200 |
| Impact Strength (kJ/m²) | 5.5 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.