Cat No:CRSM-0004
Description
High-performance semi-aromatic polyamide with glass reinforcement, offering extreme strength and low sensitivity to moisture at high temps.
| Base Material | Polyphthalamide |
| Reinforcement Type | Micro-Glass Fiber |
| Reinforcement Volume (%) | 0.3 |
| Density (g/cm³) | 1.42 |
| Tensile Strength (MPa) | 145 |
| Tensile Modulus (MPa) | 9200 |
| Elongation at Break (%) | 2.5 |
| Flexural Strength (MPa) | 215 |
| Flexural Modulus (MPa) | 8800 |
| Heat Deflection Temp (0.45MPa) | 245 |
| Glass Transition Temp (Tg) | 125 |
| Melting Point (°C) | 310 |
| Thermal Conductivity (W/mK) | 0.31 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^14 |
| Water Absorption (%) | 0.4 |
| Printing Temp (°C) | 300-330 |
| Bed Temp (°C) | 100-120 |
| Chamber Temp (°C) | 80-100 |
| Fan Speed (%) | 10 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.4 |
| Continuous Use Temp (°C) | 165 |
| Impact Strength (kJ/m²) | 12 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.