Cat No:CRSM-0068
Description
Ultra-lightweight syntactic foam composite with hollow glass microballoons, offering low dielectric constant and high buoyancy for marine research.
| Base Material | Polypropylene |
| Reinforcement Type | Hollow Glass Spheres |
| Reinforcement Volume (%) | 0.2 |
| Density (g/cm³) | 0.82 |
| Tensile Strength (MPa) | 28 |
| Tensile Modulus (MPa) | 2100 |
| Elongation at Break (%) | 8 |
| Flexural Strength (MPa) | 45 |
| Flexural Modulus (MPa) | 1850 |
| Heat Deflection Temp (0.45MPa) | 115 |
| Glass Transition Temp (Tg) | -15 |
| Melting Point (°C) | 165 |
| Thermal Conductivity (W/mK) | 0.15 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^16 |
| Water Absorption (%) | 0.05 |
| Printing Temp (°C) | 230-265 |
| Bed Temp (°C) | 85-115 |
| Chamber Temp (°C) | 50-80 |
| Fan Speed (%) | 20 |
| Nozzle Type | Stainless Steel |
| Layer Height (mm) | 0.3 |
| Shrinkage Rate (%) | 0.5 |
| Continuous Use Temp (°C) | 105 |
| Impact Strength (kJ/m²) | 12 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.