Cat No:CRSM-0037
Description
Self-lubricating composite reinforced with graphite to reduce friction and wear in gears, bearings, and sliding mechanical assemblies.
| Base Material | Polyamide 6/66 |
| Reinforcement Type | Graphite Flakes |
| Reinforcement Volume (%) | 0.1 |
| Density (g/cm³) | 1.18 |
| Tensile Strength (MPa) | 65 |
| Tensile Modulus (MPa) | 3800 |
| Elongation at Break (%) | 15 |
| Flexural Strength (MPa) | 90 |
| Flexural Modulus (MPa) | 3400 |
| Heat Deflection Temp (0.45MPa) | 170 |
| Glass Transition Temp (Tg) | 60 |
| Melting Point (°C) | 215 |
| Thermal Conductivity (W/mK) | 0.48 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^10 |
| Water Absorption (%) | 0.85 |
| Printing Temp (°C) | 250-280 |
| Bed Temp (°C) | 70-90 |
| Chamber Temp (°C) | 40-60 |
| Fan Speed (%) | 30 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.15 |
| Shrinkage Rate (%) | 0.5 |
| Continuous Use Temp (°C) | 130 |
| Impact Strength (kJ/m²) | 25 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|