| Technical Description | A 100% bio-based heat-resistant raw material with superior aroma barrier properties, designed for hot-fill luxury consumer beverage tools. |
| Base Polymer | Bio-PEF (Modified) |
| Density (g/cm3) | 1.45 |
| Tensile Strength (MPa) | 75 |
| Flexural Modulus (MPa) | 3500 |
| Elongation at Break (%) | 4.5 |
| Izod Impact Strength (J/m) | 45 |
| Glass Transition Temp (°C) | 115 |
| Melting Point (°C) | 215 |
| Printing Temp (°C) | 255 - 280 |
| Build Plate Temp (°C) | 85 - 105 |
| Thermal Conductivity (W/m⋅K) | 0.22 |
| Water Absorption (%) | 0.25 |
| Linear Mold Shrinkage (%) | 1.2 |
| Hardness (Shore D) | 85 |
| Odor Level | Near Zero |
| Chemical Resistance | Exceptional (Gas) |
| UV Stability | Superior |
| Transparency Level | 0.9 |
| Surface Tension (mN/m) | 40 |
| Recommended Speed (mm/s) | 30 - 55 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Fan Cooling (%) | 100 |
| Shelf Life (Months) | 12 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Hot-Fill Eco-Packaging |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.