| Technical Description | A bio-based raw material derived from wood pulp, offering high transparency and a premium feel for high-end consumer eyewear and fashion accessories. |
| Base Polymer | Bio-Cellulose (CA) |
| Density (g/cm3) | 1.28 |
| Tensile Strength (MPa) | 45 |
| Flexural Modulus (MPa) | 2400 |
| Elongation at Break (%) | 15 |
| Izod Impact Strength (J/m) | 45 |
| Glass Transition Temp (°C) | 95 |
| Melting Point (°C) | 190 |
| Printing Temp (°C) | 210 - 235 |
| Build Plate Temp (°C) | 50 - 70 |
| Thermal Conductivity (W/m⋅K) | 0.17 |
| Water Absorption (%) | 1.5 |
| Linear Mold Shrinkage (%) | 0.4 |
| Hardness (Shore D) | 80 |
| Odor Level | Mild Vinegar |
| Chemical Resistance | Alcohol Resistant |
| UV Stability | High |
| Transparency Level | 0.92 |
| Surface Tension (mN/m) | 38 |
| Recommended Speed (mm/s) | 25 - 45 |
| Layer Resolution (mm) | 0.10 - 0.25 |
| Fan Cooling (%) | 30 |
| Shelf Life (Months) | 12 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Luxury Eyewear Frames |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.