| Technical Description | A high-performance bio-based nylon raw material with low water absorption and high thermal stability, ideal for consumer coffee and tea equipment. |
| Base Polymer | PA 6/10 (Bio-source) |
| Density (g/cm3) | 1.08 |
| Tensile Strength (MPa) | 62 |
| Flexural Modulus (MPa) | 2100 |
| Elongation at Break (%) | 100 |
| Izod Impact Strength (J/m) | 130 |
| Glass Transition Temp (°C) | 55 |
| Melting Point (°C) | 215 |
| Printing Temp (°C) | 250 - 275 |
| Build Plate Temp (°C) | 85 - 105 |
| Thermal Conductivity (W/m⋅K) | 0.24 |
| Water Absorption (%) | 0.45 |
| Linear Mold Shrinkage (%) | 1.2 |
| Hardness (Shore D) | 76 |
| Odor Level | Neutral |
| Chemical Resistance | High (Chem) |
| UV Stability | High |
| Transparency Level | Translucent |
| Surface Tension (mN/m) | 41 |
| Recommended Speed (mm/s) | 30 - 50 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Shelf Life (Months) | 18 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Hot-Water Beverage Tools |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.