| Technical Description | A transparent, amorphous high-heat polymer with inherent UV stability, designed for consumer beverage equipment and luxury outdoor lighting. |
| Base Polymer | Polyarylate |
| Density (g/cm3) | 1.21 |
| Tensile Strength (MPa) | 70 |
| Flexural Modulus (MPa) | 2200 |
| Elongation at Break (%) | 45 |
| Izod Impact Strength (J/m) | 180 |
| Glass Transition Temp (°C) | 193 |
| Melting Point (°C) | N/A |
| Printing Temp (°C) | 320 - 350 |
| Build Plate Temp (°C) | 110 - 140 |
| Thermal Conductivity (W/m⋅K) | 0.2 |
| Water Absorption (%) | 0.25 |
| Linear Mold Shrinkage (%) | 0.65 |
| Hardness (Shore D) | 82 |
| Odor Level | None |
| Chemical Resistance | High (UV/Steam) |
| UV Stability | Superior |
| Transparency Level | 0.89 |
| Surface Tension (mN/m) | 42 |
| Recommended Speed (mm/s) | 20 - 40 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Shelf Life (Months) | 36 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | High-End Light Lenses |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.