| Technical Description | A refined corn-starch derived thermoplastic designed for high-resolution printing of kitchenware and consumer goods prototypes with minimal warping. |
| Base Polymer | Polylactic Acid (PLA) |
| Density (g/cm3) | 1.24 |
| Tensile Strength (MPa) | 62 |
| Flexural Modulus (MPa) | 3500 |
| Elongation at Break (%) | 5.5 |
| Izod Impact Strength (J/m) | 30 |
| Glass Transition Temp (°C) | 58 |
| Melting Point (°C) | 155 |
| Printing Temp (°C) | 195 - 215 |
| Build Plate Temp (°C) | 45 - 60 |
| Thermal Conductivity (W/m⋅K) | 0.13 |
| Water Absorption (%) | 0.52 |
| Linear Mold Shrinkage (%) | 0.35 |
| Hardness (Shore D) | 82 |
| Odor Level | Extremely Low |
| Chemical Resistance | Low |
| UV Stability | Moderate |
| Transparency Level | Semi-Opaque |
| Surface Tension (mN/m) | 38 |
| Recommended Speed (mm/s) | 50 - 100 |
| Layer Resolution (mm) | 0.05 - 0.20 |
| Fan Cooling (%) | 100 |
| Shelf Life (Months) | 24 |
| Raw Material Diameter (mm) | 1.75 / 2.85 |
| Primary Application | Food Packaging Prototypes |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.