Cat No:SSM-0159
Description
Alumina-matrix sacrificial core for reactive casting; survives extreme heat and allows easy chemical leaching post-process.
| Base Material | Al2O3-Binder |
| Solubility Method | Pyrolysis |
| Solvent Type | Vacuum Bake |
| Heat Deflection Temp (0.45MPa) | 650+ |
| Glass Transition Temp (Tg) | - |
| Melting Point (°C) | - |
| Density (g/cm³) | 2.9 |
| Water Absorption (%) | 0.01 |
| Tensile Strength (MPa) | 48 |
| Tensile Modulus (MPa) | 12000 |
| Elongation at Break (%) | 0.2 |
| Flexural Strength (MPa) | 90 |
| Flexural Modulus (MPa) | 11500 |
| Printing Temp (°C) | 350-400 |
| Bed Temp (°C) | 150-180 |
| Chamber Temp (°C) | 140-170 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.1 |
| Shrinkage Rate (%) | 0.01 |
| Continuous Use Temp (°C) | 600 |
| Impact Strength (kJ/m²) | 2 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|