Description
High-impact PA66 composite with aramid reinforcement, offering extreme abrasion resistance and non-brittle failure for mechanical tools.
| Base Material | Polyamide 66 |
| Reinforcement Type | Para-aramid Fiber |
| Reinforcement Volume (%) | 0.2 |
| Density (g/cm³) | 1.22 |
| Tensile Strength (MPa) | 95 |
| Tensile Modulus (MPa) | 5500 |
| Elongation at Break (%) | 8.5 |
| Flexural Strength (MPa) | 145 |
| Flexural Modulus (MPa) | 4800 |
| Heat Deflection Temp (0.45MPa) | 195 |
| Glass Transition Temp (Tg) | 70 |
| Melting Point (°C) | 260 |
| Thermal Conductivity (W/mK) | 0.24 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^14 |
| Water Absorption (%) | 0.95 |
| Printing Temp (°C) | 270-300 |
| Bed Temp (°C) | 80-110 |
| Chamber Temp (°C) | 60-90 |
| Fan Speed (%) | 20 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.5 |
| Continuous Use Temp (°C) | 150 |
| Impact Strength (kJ/m²) | 28 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.