Cat No:CRSM-0010
Description
High-stiffness PET composite utilizing long-glass fibers for superior impact strength and thermal performance over standard PETG.
| Base Material | Polyethylene Terephthalate |
| Reinforcement Type | Long-glass Fiber |
| Reinforcement Volume (%) | 0.3 |
| Density (g/cm³) | 1.55 |
| Tensile Strength (MPa) | 105 |
| Tensile Modulus (MPa) | 8200 |
| Elongation at Break (%) | 2.5 |
| Flexural Strength (MPa) | 165 |
| Flexural Modulus (MPa) | 7800 |
| Heat Deflection Temp (0.45MPa) | 195 |
| Glass Transition Temp (Tg) | 75 |
| Melting Point (°C) | 255 |
| Thermal Conductivity (W/mK) | 0.26 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^15 |
| Water Absorption (%) | 0.15 |
| Printing Temp (°C) | 280-310 |
| Bed Temp (°C) | 80-100 |
| Chamber Temp (°C) | 60-80 |
| Fan Speed (%) | 20 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.25 |
| Continuous Use Temp (°C) | 155 |
| Impact Strength (kJ/m²) | 25 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.