| Technical Description | A high-density raw material providing a premium weighted feel and high stiffness for luxury consumer product displays and packaging. |
| Base Polymer | PETG + Talc/Barium |
| Density (g/cm3) | 1.95 |
| Tensile Strength (MPa) | 42 |
| Flexural Modulus (MPa) | 4200 |
| Elongation at Break (%) | 5 |
| Izod Impact Strength (J/m) | 22 |
| Glass Transition Temp (°C) | 80 |
| Melting Point (°C) | 235 |
| Printing Temp (°C) | 240 - 265 |
| Build Plate Temp (°C) | 75 - 95 |
| Thermal Conductivity (W/m⋅K) | 0.38 |
| Water Absorption (%) | 0.12 |
| Linear Mold Shrinkage (%) | 0.35 |
| Hardness (Shore D) | 84 |
| Odor Level | Very Low |
| Chemical Resistance | High (Acids) |
| UV Stability | High |
| Transparency Level | Opaque (White) |
| Surface Tension (mN/m) | 42 |
| Recommended Speed (mm/s) | 25 - 50 |
| Layer Resolution (mm) | 0.15 - 0.35 |
| Fan Cooling (%) | 50 |
| Shelf Life (Months) | 18 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Luxury Weight Cases |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.