| Technical Description | A high-density composite providing a premium weighted feel and ceramic-like rigidity for luxury consumer cosmetic packaging. |
| Base Polymer | PLA + Barium Fill |
| Density (g/cm3) | 1.98 |
| Tensile Strength (MPa) | 40 |
| Flexural Modulus (MPa) | 5200 |
| Elongation at Break (%) | 2.5 |
| Izod Impact Strength (J/m) | 15 |
| Glass Transition Temp (°C) | 60 |
| Melting Point (°C) | 170 |
| Printing Temp (°C) | 210 - 240 |
| Build Plate Temp (°C) | 55 - 70 |
| Thermal Conductivity (W/m⋅K) | 0.38 |
| Water Absorption (%) | 0.4 |
| Linear Mold Shrinkage (%) | 0.12 |
| Hardness (Shore D) | 87 |
| Odor Level | Very Low |
| Chemical Resistance | Low |
| UV Stability | Moderate |
| Transparency Level | Opaque (White) |
| Surface Tension (mN/m) | 42 |
| Recommended Speed (mm/s) | 30 - 55 |
| Layer Resolution (mm) | 0.15 - 0.35 |
| Fan Cooling (%) | 100 |
| Shelf Life (Months) | 18 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Luxury Fragrance Bases |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.