| Technical Description | A specialized liquid raw material designed for investment casting of luxury consumer jewelry, leaving zero ash residue during the burnout process. |
| Base Polymer | Photopolymer Wax |
| Density (g/cm3) | 1.1 |
| Tensile Strength (MPa) | 25 |
| Flexural Modulus (MPa) | 800 |
| Elongation at Break (%) | 5 |
| Izod Impact Strength (J/m) | 10 |
| Glass Transition Temp (°C) | 65 |
| Melting Point (°C) | N/A |
| Printing Temp (°C) | Ambient |
| Build Plate Temp (°C) | N/A |
| Thermal Conductivity (W/m⋅K) | 0.15 |
| Water Absorption (%) | 0.25 |
| Linear Mold Shrinkage (%) | 0.8 |
| Hardness (Shore D) | 65D |
| Odor Level | Low |
| Chemical Resistance | Low |
| UV Stability | Moderate |
| Transparency Level | Opaque Blue |
| Surface Tension (mN/m) | 34 |
| Recommended Speed (mm/s) | 10-25s/layer |
| Layer Resolution (mm) | 0.025 - 0.05 |
| Fan Cooling (%) | N/A |
| Shelf Life (Months) | 12 |
| Raw Material Diameter (mm) | Liquid |
| Primary Application | Fine Jewelry Casting |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.