Cat No:CRSM-0110
Description
Smart piezoelectric composite for sensing and energy harvesting applications in flexible electronic research.
| Base Material | Polyvinylidene Fluoride |
| Reinforcement Type | Lead Zirconate Titanate |
| Reinforcement Volume (%) | 0.3 |
| Density (g/cm³) | 2.15 |
| Tensile Strength (MPa) | 35 |
| Tensile Modulus (MPa) | 2800 |
| Elongation at Break (%) | 2.5 |
| Flexural Strength (MPa) | 55 |
| Flexural Modulus (MPa) | 2400 |
| Heat Deflection Temp (0.45MPa) | 110 |
| Glass Transition Temp (Tg) | -35 |
| Melting Point (°C) | 170 |
| Thermal Conductivity (W/mK) | 0.35 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^14 |
| Water Absorption (%) | 0.03 |
| Printing Temp (°C) | 240-270 |
| Bed Temp (°C) | 80-100 |
| Chamber Temp (°C) | 40-70 |
| Fan Speed (%) | 20 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.15 |
| Shrinkage Rate (%) | 0.8 |
| Continuous Use Temp (°C) | 90 |
| Impact Strength (kJ/m²) | 5.5 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|