| Technical Description | A 100% bio-sourced self-lubricating raw material with low friction coefficients for moving parts in high-end consumer appliances. |
| Base Polymer | Polyamide 11 + MoS2 |
| Density (g/cm3) | 1.1 |
| Tensile Strength (MPa) | 50 |
| Flexural Modulus (MPa) | 1400 |
| Elongation at Break (%) | 180 |
| Izod Impact Strength (J/m) | 150 |
| Glass Transition Temp (°C) | 45 |
| Melting Point (°C) | 190 |
| Printing Temp (°C) | 245 - 275 |
| Build Plate Temp (°C) | 80 - 100 |
| Thermal Conductivity (W/m⋅K) | 0.28 |
| Water Absorption (%) | 0.18 |
| Linear Mold Shrinkage (%) | 1.3 |
| Hardness (Shore D) | 72 |
| Odor Level | Neutral |
| Chemical Resistance | Excellent |
| UV Stability | Superior |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 41 |
| Recommended Speed (mm/s) | 30 - 55 |
| Layer Resolution (mm) | 0.15 - 0.30 |
| Shelf Life (Months) | 24 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Kitchen Mixer Parts |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.