| Technical Description | A glass-reinforced nylon modified with PTFE, providing extreme stiffness and self-lubrication for heavy-duty moving parts in kitchen appliances. |
| Base Polymer | PA6 + GF + PTFE |
| Density (g/cm3) | 1.28 |
| Tensile Strength (MPa) | 115 |
| Flexural Modulus (MPa) | 7200 |
| Elongation at Break (%) | 3.5 |
| Izod Impact Strength (J/m) | 145 |
| Glass Transition Temp (°C) | 65 |
| Melting Point (°C) | 220 |
| Printing Temp (°C) | 260 - 295 |
| Build Plate Temp (°C) | 95 - 115 |
| Thermal Conductivity (W/m⋅K) | 0.38 |
| Water Absorption (%) | 1.15 |
| Linear Mold Shrinkage (%) | 0.25 |
| Hardness (Shore D) | 85 |
| Odor Level | Neutral |
| Chemical Resistance | Excellent |
| UV Stability | Moderate |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 32 |
| Recommended Speed (mm/s) | 25 - 45 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Shelf Life (Months) | 18 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | High-Load Mixer Gears |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.