| Technical Description | A partially bio-sourced nylon raw material modified with PTFE for low friction and wear resistance in high-frequency moving consumer parts. |
| Base Polymer | PA610 (Bio) + PTFE |
| Density (g/cm3) | 1.14 |
| Tensile Strength (MPa) | 55 |
| Flexural Modulus (MPa) | 2100 |
| Elongation at Break (%) | 45 |
| Izod Impact Strength (J/m) | 130 |
| Glass Transition Temp (°C) | 55 |
| Melting Point (°C) | 215 |
| Printing Temp (°C) | 250 - 280 |
| Build Plate Temp (°C) | 85 - 105 |
| Thermal Conductivity (W/m⋅K) | 0.28 |
| Water Absorption (%) | 0.4 |
| Linear Mold Shrinkage (%) | 1.1 |
| Hardness (Shore D) | 78 |
| Odor Level | Neutral |
| Chemical Resistance | Excellent |
| UV Stability | High |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 28 |
| Recommended Speed (mm/s) | 30 - 55 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Shelf Life (Months) | 18 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Coffee Grinder Bushings |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.