| Technical Description | A low-friction PBT raw material modified with PTFE to eliminate stick-slip issues in high-frequency moving consumer kitchen appliance parts. |
| Base Polymer | PBT + 15% PTFE |
| Density (g/cm3) | 1.4 |
| Tensile Strength (MPa) | 52 |
| Flexural Modulus (MPa) | 2600 |
| Elongation at Break (%) | 12 |
| Izod Impact Strength (J/m) | 55 |
| Glass Transition Temp (°C) | 60 |
| Melting Point (°C) | 225 |
| Printing Temp (°C) | 245 - 270 |
| Build Plate Temp (°C) | 70 - 90 |
| Thermal Conductivity (W/m⋅K) | 0.24 |
| Water Absorption (%) | 0.1 |
| Linear Mold Shrinkage (%) | 1.4 |
| Hardness (Shore D) | 80 |
| Odor Level | None |
| Chemical Resistance | High (Solvents) |
| UV Stability | High |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 28 |
| Recommended Speed (mm/s) | 30 - 55 |
| Layer Resolution (mm) | 0.10 - 0.25 |
| Fan Cooling (%) | 50 |
| Shelf Life (Months) | 24 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Coffee Machine Sliders |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.