Cat No:CRSM-0153
Description
Bio-based flax fiber reinforced PPS, providing an eco-friendly high-performance structural solution for industrial R&D.
| Base Material | PPS |
| Reinforcement Type | Flax Fiber |
| Reinforcement Volume (%) | 0.25 |
| Density (g/cm³) | 1.28 |
| Tensile Strength (MPa) | 75 |
| Tensile Modulus (MPa) | 6200 |
| Elongation at Break (%) | 2.2 |
| Flexural Strength (MPa) | 115 |
| Flexural Modulus (MPa) | 5800 |
| Heat Deflection Temp (0.45MPa) | 240 |
| Glass Transition Temp (Tg) | 95 |
| Melting Point (°C) | 285 |
| Thermal Conductivity (W/mK) | 0.22 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^16 |
| Water Absorption (%) | 0.1 |
| Printing Temp (°C) | 320-350 |
| Bed Temp (°C) | 110-130 |
| Chamber Temp (°C) | 90-110 |
| Fan Speed (%) | 10 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.25 |
| Continuous Use Temp (°C) | 210 |
| Impact Strength (kJ/m²) | 9.5 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.