Cat No:CRSM-0165
Description
High-stiffness GF-PA12 composite for structural aerospace brackets and industrial automation parts in variable humidity.
| Base Material | Polyamide 12 |
| Reinforcement Type | Micro-Glass Fiber |
| Reinforcement Volume (%) | 0.3 |
| Density (g/cm³) | 1.42 |
| Tensile Strength (MPa) | 85 |
| Tensile Modulus (MPa) | 6500 |
| Elongation at Break (%) | 2.5 |
| Flexural Strength (MPa) | 135 |
| Flexural Modulus (MPa) | 5800 |
| Heat Deflection Temp (0.45MPa) | 165 |
| Glass Transition Temp (Tg) | 45 |
| Melting Point (°C) | 178 |
| Thermal Conductivity (W/mK) | 0.35 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^15 |
| Water Absorption (%) | 0.55 |
| Printing Temp (°C) | 250-280 |
| Bed Temp (°C) | 80-100 |
| Chamber Temp (°C) | 50-70 |
| Fan Speed (%) | 20 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.35 |
| Continuous Use Temp (°C) | 115 |
| Impact Strength (kJ/m²) | 16 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.