Cat No:SSM-0037
Description
Ultra-low ash graphite support designed for supporting titanium or nickel-based superalloys during the high-heat binder jetting/sintering process.
| Base Material | Graphite-Polymer Blend |
| Solubility Method | Thermal |
| Solvent Type | Pyrolysis |
| Heat Deflection Temp (0.45MPa) | 300+ |
| Glass Transition Temp (Tg) | 320 |
| Melting Point (°C) | - |
| Density (g/cm³) | 0.92 |
| Water Absorption (%) | 0.01 |
| Tensile Strength (MPa) | 35 |
| Tensile Modulus (MPa) | 4800 |
| Elongation at Break (%) | 0.8 |
| Flexural Strength (MPa) | 62 |
| Flexural Modulus (MPa) | 4500 |
| Printing Temp (°C) | 330-370 |
| Bed Temp (°C) | 130-160 |
| Chamber Temp (°C) | 110-150 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.01 |
| Continuous Use Temp (°C) | 280 |
| Impact Strength (kJ/m²) | 3.8 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^5 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|