Cat No:CRSM-0095
Description
Metal-fiber reinforced PLA for magnetic receptivity and thermal conductivity applications in laboratory equipment prototyping.
| Base Material | PLA |
| Reinforcement Type | 316L Stainless Steel Fiber |
| Reinforcement Volume (%) | 0.15 |
| Density (g/cm³) | 1.95 |
| Tensile Strength (MPa) | 42 |
| Tensile Modulus (MPa) | 4200 |
| Elongation at Break (%) | 1.5 |
| Flexural Strength (MPa) | 75 |
| Flexural Modulus (MPa) | 3800 |
| Heat Deflection Temp (0.45MPa) | 58 |
| Glass Transition Temp (Tg) | 60 |
| Melting Point (°C) | 165 |
| Thermal Conductivity (W/mK) | 1.5 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^2 |
| Water Absorption (%) | 0.1 |
| Printing Temp (°C) | 200-230 |
| Bed Temp (°C) | 50-60 |
| Chamber Temp (°C) | - |
| Fan Speed (%) | 100 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.15 |
| Shrinkage Rate (%) | 0.1 |
| Continuous Use Temp (°C) | 50 |
| Impact Strength (kJ/m²) | 4.5 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.