Carbon-fiber-reinforced breakaway support for large-scale composite-polyester prints requiring high rigidity and clean mechanical peeling.
| Base Material | CF-Reinforced Co-Polymer |
| Solubility Method | Mechanical |
| Solvent Type | None |
| Heat Deflection Temp (0.45MPa) | 120 |
| Glass Transition Temp (Tg) | 130 |
| Melting Point (°C) | 240 |
| Density (g/cm³) | 1.35 |
| Water Absorption (%) | 0.1 |
| Tensile Strength (MPa) | 78 |
| Tensile Modulus (MPa) | 7200 |
| Elongation at Break (%) | 2.5 |
| Flexural Strength (MPa) | 125 |
| Flexural Modulus (MPa) | 6800 |
| Printing Temp (°C) | 260-290 |
| Bed Temp (°C) | 100-130 |
| Chamber Temp (°C) | 80-110 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.15 |
| Shrinkage Rate (%) | 0.15 |
| Continuous Use Temp (°C) | 115 |
| Impact Strength (kJ/m²) | 18 |
| Flame Retardancy (UL94) | V-1 |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.