Cat No:CRSM-0036
Description
Cost-effective industrial composite providing high dimensional stability and heat resistance for large-scale automotive jigs and fixtures.
| Base Material | Polypropylene |
| Reinforcement Type | Mineral Talc |
| Reinforcement Volume (%) | 0.2 |
| Density (g/cm³) | 1.08 |
| Tensile Strength (MPa) | 32 |
| Tensile Modulus (MPa) | 3500 |
| Elongation at Break (%) | 10 |
| Flexural Strength (MPa) | 52 |
| Flexural Modulus (MPa) | 3200 |
| Heat Deflection Temp (0.45MPa) | 125 |
| Glass Transition Temp (Tg) | -15 |
| Melting Point (°C) | 165 |
| Thermal Conductivity (W/mK) | 0.22 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^15 |
| Water Absorption (%) | 0.02 |
| Printing Temp (°C) | 230-260 |
| Bed Temp (°C) | 90-110 |
| Chamber Temp (°C) | 50-70 |
| Fan Speed (%) | 20 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.2 |
| Shrinkage Rate (%) | 0.6 |
| Continuous Use Temp (°C) | 105 |
| Impact Strength (kJ/m²) | 14 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|