| Technical Description | A glass-fiber reinforced raw material sourced from recycled Nylon 6, offering high mechanical strength for structural consumer gear. |
| Base Polymer | rPA6 + 15% Glass Fiber |
| Density (g/cm3) | 1.25 |
| Tensile Strength (MPa) | 105 |
| Flexural Modulus (MPa) | 6500 |
| Elongation at Break (%) | 3.5 |
| Izod Impact Strength (J/m) | 115 |
| Glass Transition Temp (°C) | 65 |
| Melting Point (°C) | 220 |
| Printing Temp (°C) | 260 - 290 |
| Build Plate Temp (°C) | 90 - 110 |
| Thermal Conductivity (W/m⋅K) | 0.42 |
| Water Absorption (%) | 1.2 |
| Linear Mold Shrinkage (%) | 0.25 |
| Hardness (Shore D) | 84 |
| Odor Level | Neutral |
| Chemical Resistance | Excellent |
| UV Stability | Moderate |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 45 |
| Recommended Speed (mm/s) | 25 - 45 |
| Layer Resolution (mm) | 0.10 - 0.20 |
| Shelf Life (Months) | 18 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Sustainable Brackets |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.