| Technical Description | A vulcanized thermoplastic elastomer raw material providing rubber-like durability and heat resistance for consumer products requiring soft ergonomic grips. |
| Base Polymer | TPV (Vulcanized) |
| Density (g/cm3) | 0.98 |
| Tensile Strength (MPa) | 10 |
| Flexural Modulus (MPa) | 12 |
| Elongation at Break (%) | >500 |
| Izod Impact Strength (J/m) | No Break |
| Glass Transition Temp (°C) | -60 |
| Melting Point (°C) | 160 |
| Printing Temp (°C) | 220 - 245 |
| Build Plate Temp (°C) | 20 - 50 |
| Thermal Conductivity (W/m⋅K) | 0.15 |
| Water Absorption (%) | 0.08 |
| Linear Mold Shrinkage (%) | 2.5 |
| Hardness (Shore D) | 45A |
| Odor Level | Characteristic |
| Chemical Resistance | Acid/Alkali Res. |
| UV Stability | Very High |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 28 |
| Recommended Speed (mm/s) | 15 - 30 |
| Layer Resolution (mm) | 0.20 - 0.40 |
| Fan Cooling (%) | 20 |
| Shelf Life (Months) | 24 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Soft-Touch Bottle Grips |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.