Cat No:SSM-0113
Description
Hybrid wax-ceramic sacrificial for fine investment casting; reduces metal-mold reaction and improves final surface quality.
| Base Material | Wax-Alumina Blend |
| Solubility Method | Thermal |
| Solvent Type | Burnout |
| Heat Deflection Temp (0.45MPa) | 150 |
| Glass Transition Temp (Tg) | - |
| Melting Point (°C) | 180 |
| Density (g/cm³) | 1.8 |
| Water Absorption (%) | 0.01 |
| Tensile Strength (MPa) | 15 |
| Tensile Modulus (MPa) | 2500 |
| Elongation at Break (%) | 1 |
| Flexural Strength (MPa) | 35 |
| Flexural Modulus (MPa) | 2200 |
| Printing Temp (°C) | 180-220 |
| Bed Temp (°C) | 40-70 |
| Chamber Temp (°C) | 30-50 |
| Fan Speed (%) | 100 |
| Nozzle Type | Brass |
| Layer Height (mm) | 0.1 |
| Shrinkage Rate (%) | 0.5 |
| Continuous Use Temp (°C) | 130 |
| Impact Strength (kJ/m²) | 2 |
| Flame Retardancy (UL94) | HB |
| Surface Resistivity (Ω) | 10^15 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.