| Technical Description | An eco-sourced raw material combining bio-polymers with recycled wood fibers, providing a natural aesthetic and texture for sustainable consumer goods. |
| Base Polymer | PLA + 40% Wood Fiber |
| Density (g/cm3) | 1.15 |
| Tensile Strength (MPa) | 35 |
| Flexural Modulus (MPa) | 3600 |
| Elongation at Break (%) | 3 |
| Izod Impact Strength (J/m) | 18 |
| Glass Transition Temp (°C) | 58 |
| Melting Point (°C) | 155 |
| Printing Temp (°C) | 190 - 220 |
| Build Plate Temp (°C) | 50 - 65 |
| Thermal Conductivity (W/m⋅K) | 0.15 |
| Water Absorption (%) | 1.1 |
| Linear Mold Shrinkage (%) | 0.2 |
| Hardness (Shore D) | 78 |
| Odor Level | Natural Wood |
| Chemical Resistance | Low |
| UV Stability | Moderate |
| Transparency Level | Opaque |
| Surface Tension (mN/m) | 36 |
| Recommended Speed (mm/s) | 30 - 60 |
| Layer Resolution (mm) | 0.15 - 0.30 |
| Fan Cooling (%) | 100 |
| Shelf Life (Months) | 12 |
| Raw Material Diameter (mm) | 1.75 |
| Primary Application | Sustainable Home Decor |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.