Ceramic composite feedstock for high-toughness components, combining the hardness of alumina with the crack resistance of zirconia.
| Base Material | Alumina/Zirconia |
| Reinforcement Type | Al2O3 + ZrO2 |
| Reinforcement Volume (%) | 0.5 |
| Density (g/cm³) | 3.2 |
| Tensile Strength (MPa) | 280 |
| Tensile Modulus (MPa) | 15500 |
| Elongation at Break (%) | 0.8 |
| Flexural Strength (MPa) | 310 |
| Flexural Modulus (MPa) | 14200 |
| Heat Deflection Temp (0.45MPa) | 400 |
| Glass Transition Temp (Tg) | - |
| Melting Point (°C) | 2000 |
| Thermal Conductivity (W/mK) | 24 |
| Flame Retardancy (UL94) | V-0 |
| Surface Resistivity (Ω) | 10^16 |
| Water Absorption (%) | 0.02 |
| Printing Temp (°C) | 240-270 |
| Bed Temp (°C) | 90-110 |
| Chamber Temp (°C) | - |
| Fan Speed (%) | 15 |
| Nozzle Type | Hardened Steel |
| Layer Height (mm) | 0.1 |
| Shrinkage Rate (%) | 18 |
| Continuous Use Temp (°C) | 1600 |
| Impact Strength (kJ/m²) | 6.5 |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
For Research or Industrial Raw Materials, Not For Personal Medical Use!
|
There is no product in your cart. |
Eata 3DPrint: Your innovation partner for advanced 3D printing solutions, delivering cutting-edge services and materials to transform industries and drive progress.
Enter your E-mail and receive the latest news from us.