High-Concentration Salt

Cat No:BME-0008

Description

A "solvent-in-salt" electrolyte using LiFSI to expand the voltage window and prevent aluminum current collector corrosion at high potentials.

Datasheet

Inquiry

Basic Information

Main Salt	LiFSI
Salt Concentration	3.0 M
Solvent Ratio (Vol%)	DMC
Additive 1	N/A
Additive 2	N/A
Appearance	Slightly Yellow
Water Content (KF)	≤ 30 ppm
Free Acid (as HF)	≤ 60 ppm
Density (25°C)	1.40-1.50 g/cm³
Conductivity (25°C)	5.0-7.0 mS/cm
Viscosity (25°C)	10-20 mPa·s
Chloride (Cl-)	≤ 2 ppm
Sulfate (SO4 2-)	≤ 10 ppm
Iron (Fe) Content	≤ 2 ppm
Sodium (Na) Content	≤ 5 ppm
Potassium (K) Content	≤ 5 ppm
Operating Voltage	0.0 - 5.0 V
Operating Temp	0 to 60°C
Flash Point	15-25°C
Solid Content	35-45 wt%
Refractive Index	1.42-1.52
Turbidity	≤ 15 NTU
Color (APHA)	≤ 100
Packaging	Glass/SS
Storage	< 5°C, Ar