LATP Solid-State Battery Electrolyte Sheet (12 mm x 260 um, >= 0.45 mS/cm)

Cat No:BMSPEM-0714

Description

This pre-sintered lithium aluminum titanium phosphate electrolyte sheet from Eata Battery is ready for direct cell assembly without pressing or sintering. Specifications: chemical formula Li1.3Al0.3Ti1.7P3O12; theoretical ionic conductivity 2 x 10^-4 S/cm; ceramic sample ionic conductivity >= 0.45 mS/cm at 25 C by AC impedance; theoretical density 2.94 g/cm3 with measured density >= 2.793 g/cm3 (drainage method); densification >= 95%; flexural strength >= 130 MPa by three-point bending; thickness 260 +/- 10 um; diameter 12 +/- 0.1 mm; square format 60 x 60 mm and other sizes customizable; appearance white with uniform color; main crystal phase consistent with the characteristic peaks of PDF#35-0754 by XRD; micromorphology at 20,000x magnification with no more than 3 holes by SEM; shelf life 1 year. Compared with powder routes requiring pressing and 1100-1200 C sintering, the pre-sintered sheet reaches a testable cell within hours.